Polystyrene
Melt Volume Rate 200°C, 5 kg cm³/10 min 3.8 1133 H
Melt Flow Rate 200°C, 5 kg g/10 min 4 1133 H
Vi cat softening point B/50 ° C 94 306 B50
HDT/A 1.8MPa ° C 77 75 -1& -2Af
Charpy Unnotched Impact at 23 °C kJ/m² No Break 179/1eU
Charpy Notched Impact at 23 °C kJ/m² 12 179/1eA
Flexural Modulus MPa 1900 178
Flexural Strength MPa 45 178
Tensile Modulus MPa 1750 527 –1& -2/1A/1
Tensile stress at yield MPa 25 527 –1& -2/1A/50
Tensile strain at yield % 0.6 527 –1& -2/1A/50
Tensile stress at break MPa 50 527 –1& -2/1A/50
Tensile strain at break % 25 527 –1& -2/1A/50
Density at 23 °C kg/m³ 1.04 1183
Moulding shrinkage % 0.3 294-4